EW100 fiber glass cloth/fabric is widely used in aerospace industry, shipbuilding industry, medical industry, chemical industry, military industry, sports goods and other fields. It can be used to produce mica belts, fishing rods, golf clubs, baseball clubs, surfboards, sailboards, boat hulls, FRP water tanks, swimming pools, car bodies, FRP pipes and other FRP products.
Item | Unit | TYPE: XG100 |
0.1mm | ||
Standard | ||
Width | mm | 1000±10 |
Length | m | 1050±10 |
Thickness | mm | 0.1±0.01 |
Weight per unit area | g/m2 | 100±8 |
No. of threads warp | cm-1 | 21±1 |
No. of threads weft | cm-1 | 16±1 |
Tensile strength warp | N/cm | ≥250 |
Tension strength Weft | N/cm | ≥230 |
Loss on ignition(1h/550℃) | % | ≤2.5 |
Weaving type | -/- | Plain |
EW100 fiber glass cloth/fabric is widely used in aerospace industry, shipbuilding industry, medical industry, chemical industry, military industry, sports goods and other fields. It can be used to produce mica belts, fishing rods, golf clubs, baseball clubs, surfboards, sailboards, boat hulls, FRP water tanks, swimming pools, car bodies, FRP pipes and other FRP products.
Item | Unit | TYPE: XG100 |
0.1mm | ||
Standard | ||
Width | mm | 1000±10 |
Length | m | 1050±10 |
Thickness | mm | 0.1±0.01 |
Weight per unit area | g/m2 | 100±8 |
No. of threads warp | cm-1 | 21±1 |
No. of threads weft | cm-1 | 16±1 |
Tensile strength warp | N/cm | ≥250 |
Tension strength Weft | N/cm | ≥230 |
Loss on ignition(1h/550℃) | % | ≤2.5 |
Weaving type | -/- | Plain |